Model NO.: KFT F 959
Filtration Grade: HEPA Filter
Filter Bag Sectional Shape: Round Bag
Filter Bag Environment: High-Temperature
Cartridge Installation: Specific Angle Ramp Loading
Woven Pattern: Double Twill
Weight of Finished of Product (G/M2): 760+20
Thickness (mm): 0.8+0.05
Tensile Strength(N/25*100): Warp :2700 Wlft:2700
Filter Wind′speed(M/Min): Less Than or Equal 1.0
Air Permeability(Cm3/Cm2·s): 3-5
Elongation: Warp: Less Than Equal 2 Welf : More Than Equal 2
Application: Cement Plant , Burning Coal Boiler
Trademark: defender of blue sky
Transport Package: Carton Box: 550X550X550mm
Specification: Custiomized
Origin: China
HS Code: 5911400000
production descriptionÂ
   Fluorosilicone fiber is s new filtering materials developed by us which can be widely used in the industry of coal burning furnace, biomass power furnace , coal burning generated power , kiln head and kiln tail of cement , metal smelting . long -term working temperature can be reached to 240-260 degree ,instantaneous temperature can be reached to 280 degree . it owns excellent stability in heating and chemistry as well as abrasive resistance . Modified characteristics of Fluorosilicone materials is have a strong anti-alkali and  anti-sulfer dioxide .
    This patented products filled a gap in this field of filtering materials - Thechical parameters:
| Fluorosilicone superfine modified fiber | ||
| Woven pattern | Double  twill | |
| weght(g/m²) | 760+20 | |
| thickness() | 0.8+0.05 | |
| temperature(ºC) | Working | ≤240 |
| instantaneous | <260 | |
| Tensile strength(N/25*100) | warp | ≥2700 |
| welt | ≥2700 | |
| Filter wind'speed(m/min) | ≤1.0 | |
| Air permeability(cm3/cm2·s) | 3-5 | |
| Enlongation(%) | warp | ≤2 |
| weft | ≤2 | |
| Finishing treatment | PTFEdiping,layer covered (laminating) | |
| application | Cement filed/ Â power plant . Â burning coal boiler | |